A Study on the Properties Analysis of an Iron Fittings Type CSST Damaged by the PCITS

Jang-Woo, Lee; Chung-Seog, Choi

doi:2016.30.4.121

Fire Sci. Eng. > Volume 30(4); 2016 > Article

Fire Science and Engineering 2016;30(4):121-127.
DOI: https://doi.org/10.7731/KIFSE.2016.30.4.121 Published online August 31, 2016.

PCITS에 의해 소손된 강이음쇠형 CSST의 특성 해석에 관한 연구

이장우, 최충석

¹전주대학교 소방안전공학과
²전주대학교 소방안전공학과

A Study on the Properties Analysis of an Iron Fittings Type CSST Damaged by the PCITS

Lee Jang-Woo, Choi Chung-Seog

¹Dept. of Fire Safety Engineering, Jeonju Univ.
²Dept. of Fire Safety Engineering, Jeonju Univ.

요약

본 논문에서는 대전류공급장치(PCITS)에 의해 소손된 강이음쇠형(iron fittings type) 금속플렉시블호스(CSST)의 구조 및 전기적 특성을 해석하였다. CSST는 보호 피막, 튜브, 너트, 클램프 링, 플레어 캡, 소켓, 볼 밸브 등으로 구성되어 있다. CSST의 내전압 평가는 전기 충전부와 비충전부 사이에 교류 전압 220 V를 1분간 인가하여 견뎌야 한다. 직류 500 V에 의한 절연 성능의 평가는 온도 상승 시험 전에 $1M{Omega}$ 이상, 시험이 끝난 후에는 $0.3M{Omega}$ 이상을 요구한다. 정상 제품의 평균 저항은 $11.5m{Omega}$이었으나 PCITS로 130 A를 흘려 소손된 제품의 평균 저항 $11.50m{Omega}$이었다. 또한 130 A가 약 10 s 흘렀을 때 튜브의 보호 피막이 일부 용융되었고, 검정색의 연기가 발생하였다. 60 s 경과되면 튜브의 대부분이 적색으로 발열되며, 전류가 120 s 흘렀을 때는 적열 범위가 넓어졌다. 95%의 신뢰 구간(CI)의 검증에서 P 값은 0.019로 정규 분포를 갖지 못하였으나 Anderson-Darling (AD) 통계량은 0.896, 표준 편차는 0.5573 등으로 양호한 특성을 나타냈다.

Abstract

This study analyzed the structural and electrical characteristics of an iron fittings type Corrugated Stainless Steel Tubing (CSST) damaged by the Primary Current Injection Test System (PCITS). CSST consists of cladding, tube, nuts, clamp ring, flare cap, socket, and ball valve. For an evaluation of the dielectric withstand voltage, the area between the live part and non-live part of the CCST shall withstand a voltage of 220 V AC for one minute. For an evaluation of the insulation performance by 500 V DC, it is required that the insulation exceed more than $1M{Omega}$ before the temperature rise test, $0.3M{Omega}$ after the test. Although the average resistance of the product was $11.5m{Omega}$, that of the product damaged at a current of 130 A by the PCITS was $11.50m{Omega}$. Furthermore, parts of the cladding were melted and black smoke appeared when a current of 130 A applied for 10 s. After 60 s, most parts were heated and turned red. At 120 s, the parts that turned red had widened. Although it did not form a normal distribution because the P value was 0.019 with a confidential interval of 95%, it revealed outstanding characteristics with an AD (Anderson-Darling) value of 0.896 and a standard deviation of 0.5573.